Effect of commercial silanes on bond strength of resin cement to lithium disilicate ceramic / Efeito de silanos comerciais na resistência de união do cimento resinoso à cerâmica de dissilicato de lítio

The aim of this study was to evaluate the effect of different commercial silanes on microshear bond strength of resin cement to lithium disilicate ceramic. Twenty ceramic samples with 10 mm in length, 10 mm wide and 3 mm in thickness were fabricated, etched with 10% hydrofluoric acid for 20 seconds, and divided into 5 groups, according to the commercial silane applied: G1- RelyX Ceramic Primer (3M ESPE), G2- Angelus Silane, G3- Prosil (FGM), G4- Dentsply Silane (Dentsply) and G5- Bis-Silane (Bisco). Silanes were applied in accordance to manufacturers' recommendations. Addition silicone molds with 1 mm in thickness, 10 mm in diameter and 3 perforations with 1 mm in diameter each one, were placed on ceramic and filled with the resin cement RelyX ARC (3M ESPE) in all groups. Light activation was performed with LED Bluephase G2 (Ivoclar Vivadent) at 1200 mW/cm2, for 30 seconds. Samples were maintained in 100% humidity at 37°C for 24 hours and submitted to microshear test. The data (MPa) were submitted to one-way ANOVA and Tukey test (α=0.05). The results obtained for each group were: G1: 22.39±2.99; G2: 23.35±4.08; G3: 26.05±5.46; G4: 18.56±4.09; G5: 25.26±4.10. Statistical analysis showed significantly lower microshear bond strength for G4. Fracture pattern analysis showed predominance of adhesive failures in G1 and G2. G3 and G5 presented higher percentage of cohesive failures in ceramic, and G4 showed mixed, adhesive and cohesive fractures with similar percentages. It was concluded that different silanes showed influence on the lithium disilicate ceramic ­ resin cement bond strength

O objetivo neste estudo foi avaliar o efeito de diferentes silanos comerciais na resistência de união ao microcisalhamento do cimento resinoso à cerâmica de dissilicato de lítio. Foram confeccionadas 20 amostras de cerâmica (10mm de comprimento, 10mm de largura e 3mm de espessura), condicionadas com ácido fluorídrico a 10% por 20 segundos e divididas em 5 grupos, de acordo com o silano aplicado: G1- RelyX Ceramic Primer (3M ESPE), G2- Silano Angelus, G3-Prosil (FGM), G4- Silano Dentsply e G5-Bis-Silane (Bisco). Matrizes de silicone por adição (1 mm de espessura, 10 mm de diâmetro e 3 perfurações com 1 mm de diâmetro) foram colocadas sobre a cerâmica e preenchidas com cimento resinoso RelyX ARC (3M ESPE). A fotoativação foi realizada com LED Bluephase G2 (Ivoclar Vivadent) a 1200 mW/cm2, por 30 segundos. As amostras foram mantidas em 100% de umidade a 37°C por 24 horas e submetidas ao teste de microcisalhamento. Os dados (MPa) (G1: 22,39+2,99; G2: 23,35+4,08; G3: 26,05+5,46; G4: 18,56+ 4,09; G5: 25,26+4,10) foram submetidos a análise de variância e ao teste de Tukey (p<0,05). A análise estatística mostrou valor de resistência de união significantemente menor para G4. A análise do padrão de fratura mostrou predominância de falha adesiva para G1 e G2. G3 e G5 apresentaram maior porcentagem de falha coesiva em cerâmica, e o G4 apresentou fraturas mista, adesiva e coesiva em igual porcentagem. Concluiu-se que os diferentes silanos apresentaram influência na resistência de união do cimento resinoso à cerâmica de dissilicato de lítio

Aged Translucent Aesthetic Zirconia: Bond Strength Analysis.

OBJECTIVE: This study evaluates the bond strength of two compositions of aesthetic translucent zirconia (TZ). MATERIALS AND METHODS: For this evaluation, test specimens were prepared from ICE Zirkon TZ and Prettau Anterior zirconia (PAZ) that were stored in distilled water at 37°C for two time periods: T1 (24 h) and T2 (90 days) to simulate aging. Two factors were evaluated for the samples-ceramic and aging time. The samples were subjected to tests of microshear strength and fracture type and were evaluated using scanning electron microscopy. RESULTS: The results were analyzed using the D'Agostino test, analysis of variance, and Tukey's test (p < 0.01). Statistically significant differences were observed for ceramic type and aging time. CONCLUSION: The results showed that PAZ provides significantly superior performance to TZ at the two aging times evaluated.

Reabilitação estética do sorriso com facetas cerâmicas ­ relato de caso / Smile aesthetic rehabilitation with ceramic veneers ­ case report

Uma das mais importantes questões da Odontologia atual é a preservação do esmalte dentário. Nesse contexto, os laminados cerâmicos apresentam excelente reprodução das propriedades ópticas da estrutura dental, especialmente em espessuras mínimas. Este artigo apresenta um caso clínico, esclarecendo indicação, vantagens, desvantagens e limitações das facetas cerâmicas. Concluiu-se que, atualmente, os laminados cerâmicos são a melhor opção de tratamento nos casos de estética elevada, uma vez que é uma reabilitação conservadora que imita fielmente a estrutura dental e sua forma (AU).

One of the most important issues of today's Dentistry is the preservation of sound enamel. In this context, ceramic veneers present excellent reproduction of the optical properties of the dental structure, especially in minimal thicknesses. The current article aims to present a case report, clarifying the indication, advantages, disadvantages, and limitations of laminate veneers. We concluded that the ceramic veneers are currently the best treatment option for elective aesthetic cases, once it is an extremely conservative rehabilitation that faithfully mimics the dental structure and shape, besides being a very predictable treatment (AU).

Restabelecimento da dimensão vertical de oclusão utilizando próteses parciais fixas ­ relato de caso / Re-establishing of occlusal vertical dimension through fixed partial prosthesis ­ clinical report

O restabelecimento da dimensão vertical de oclusão (DVO) de pacientes é uma tarefa complexa e, em virtude disso, diversos métodos são empregados, rotineiramente, na busca do correto relacionamento maxilomandibular. Sempre que indicado, o aumento da DVO deve ser feito com próteses fixas para melhor adaptação do organismo à nova condição oclusal. O presente caso clínico descreve uma situação de acentuada perda de DVO, em um paciente parcialmente edentado, com desgastes dentais severos. Depois dessa dimensão ter sido recuperada por meio de coroas provisórias, sem que houvesse presença de alterações funcionais, próteses parciais fixas foram confeccionadas. A utilização de próteses fixas no caso em questão facilitou a obtenção de uma guia canina e guia anterior mais precisas, pelo grande número de elementos pilares. O resultado final deste caso clínico comprovou a efetividade de restabelecer adequadamente a DVO perdida, por meio da confecção de coroas provisórias e próteses fixas sem causar dores e/ou desconforto ao paciente.

Reestablishment of occlusal vertical dimension (OVD) is a complex task therefore different methods are used routinely in the search of proper maxillomandibular relation. When indicated, the increasing of VDO must be done with fixed prosthesis for a better adaptation of the organism to the new occlusal condition. The reported clinical case describes a situation of severe VDO loss in a partially edentulous patient with severe dental wear. After recovery of this position through temporary prosthesis, without any major functional changes, fixed partial dentures (fPD) were used. The use of fPD, in this case has enabled a more precise canine and anterior guidance due to a large number of abutments elements. final results have proved the effectiveness of the use of temporary prosthesis and fixed prostheses proper restoration of lost VDO, without pain and/or discomfort to the patient.

Microbiological evaluation of ultrasonic nebulization for disinfecting dental impressions.

Disinfecting dental impressions is necessary to decrease the risk of cross-contamination in dental offices. Ultrasonic nebulization has been mentioned as a microbicidal technique that can be used to disinfect contaminated dental impressions. This study compared the microbicidal effect of 2% glutaraldehyde and 0.2% peracetic acid for the disinfection of dental impressions made with vinyl polysiloxane, using 2 disinfection methods: immersion and ultrasonic nebulization. Bactericial efficacy was examined using Staphylococcus aureus and Bacillus atrophaeus as indicators. Thirty impressions were obtained and distributed randomly in 5 groups (n = 6). Group 1 was immersed in 2% glutaraldehyde immersion for 10 minutes, Group 2 was immersed in 0.2% peracetic acid for 10 minutes, Group 3 underwent ultrasonic nebulization for 10 minutes in 2% glutaraldehyde solution, Group 4 underwent ultrasonic nebulization for 10 minutes in 0.2% peracetic acid solution, and Group 5 was a control group that received no disinfectant. Both solutions experienced a 100% reduction in microorganisms following ultrasonic nebulization, as did peracetic acid following immersion; however, immersion in glutaraldehyde demonstrated lower values of reduction in B atrophaeus group, with a statistically significant difference compared with the other experimental groups.

Tratamento superficial de cerâmicas reforçadas in-ceram previamente aos procedimentos de cimentação adesiva: revisão de literatura / Superficial treatment of the reinforced in ceram ceramic before the luting procedures: literature review

Desde o início do emprego das cerâmicas em restaurações indiretas, a odontologia passou a viver uma nova realidade. Na busca pelo aperfeiçoamento desses materiais surgiram as coroas protéticas de cerâmicas reforçadas por vidro, que possuem maior resistência à fratura, porém apresentam dificuldades no condicionamento superficial prévio aos procedimentos cimentadores. Objetivando apontar um protocolo de condicionamento superficial e de cimentação adesiva deste tipo de material, o presente trabalho traz uma revisão de literatura acerca das diferentes técnicas de tratamento de superfície interna de coroas protéticas de cerâmicas reforçadas por vidro. Os principais métodos empregados e que merecem ser discutidos são os jateamentos com óxido de alumínio e partículas de sílica, bem como a palicação de ácido fluorídrico e a silanização. Atualmente, as pesquisas têm apontado para a silicatização como o meio mais eficiente para prover a retenção entre este tipo de material e o remanescente dentário, quando procedimentos de cimentação adesiva são empregados. Os cimentos que possuem monômeros fosfatados também apresentam evidências de serem mais efetivos neste tipo de cimentação e têm sido indicados com sucesso.

Effect of different modes of light modulation on the bond strength and knoop hardness of a dental composite.

This study evaluated the bond strength and Knoop hardness of Z250 composite resin, light activated with XL2500 curing unit, using different protocols: continuous mode - high intensity (CH) (700 mW/cm(2)) for 20 s; continuous mode - low intensity (CL) (150 mW/cm(2)) for 20 s; and pulse-delay with 150 mW/cm(2) for 2(P2), 3(P3), 5(P5), 10(P10) or 15 s (P15), with a 1-min delay, followed by 700 mW/cm(2) for 20 s. For the push-out test (n=10), the bond strength values were obtained using a universal test machine at a crosshead speed of 0.5 mm/min. For Knoop hardness (n=5), the specimens were made using the same light-activation protocols. The hardness measurements were made with a hardness tester at six depths (top, 1, 2, 3, 4, and 5 mm). The data were subjected to ANOVA and Tukey's test at 5% significance level. For bond strength, CL and P5 presented significantly higher mean values (p<0.05) than the other groups. There was no statistically significant difference (p>0.05) between P2, P3, P10, P15 and CH. For Knoop hardness, CH and P15 presented the highest mean values from top surface up to 4 mm depth , while CL presented the lowest hardness mean values (p<0.05). From the depth of 3 mm to 5 mm, the mean values of all groups were significantly lower (p<0.05) than those recorded on top surface. In conclusion, for the pulse-delay method, the initial exposure time can influence bond strength and Knoop hardness of composites.

Effect of different modes of light modulation on the bond strength and knoop hardness of a dental composite

This study evaluated the bond strength and Knoop hardness of Z250 composite resin, light activated with XL2500 curing unit, using different protocols: continuous mode - high intensity (CH) (700 mW/cm²) for 20 s; continuous mode - low intensity (CL) (150 mW/cm²) for 20 s; and pulse-delay with 150 mW/cm² for 2(P2), 3(P3), 5(P5), 10(P10) or 15 s (P15), with a 1-min delay, followed by 700 mW/cm² for 20 s. For the push-out test (n=10), the bond strength values were obtained using a universal test machine at a crosshead speed of 0.5 mm/min. For Knoop hardness (n=5), the specimens were made using the same light-activation protocols. The hardness measurements were made with a hardness tester at six depths (top, 1, 2, 3, 4, and 5 mm). The data were subjected to ANOVA and Tukey's test at 5 percent significance level. For bond strength, CL and P5 presented significantly higher mean values (p<0.05) than the other groups. There was no statistically significant difference (p>0.05) between P2, P3, P10, P15 and CH. For Knoop hardness, CH and P15 presented the highest mean values from top surface up to 4 mm depth , while CL presented the lowest hardness mean values (p<0.05). From the depth of 3 mm to 5 mm, the mean values of all groups were significantly lower (p<0.05) than those recorded on top surface. In conclusion, for the pulse-delay method, the initial exposure time can influence bond strength and Knoop hardness of composites.

Este estudo verificou a resistência de união e a dureza Knoop do compósito Z250 (3M/ESPE), fotoativado com luz de lâmpada halógena (XL2500, 3M/ESPE), utilizando diferentes protocolos: modo contínuo alta intensidade (CH) (700mW/cm²) por 20s; modo contínuo baixa intensidade (CL) (150mW/cm²) por 20s; pulse-delay com 150mW/cm² por 2(P2), 3(P3), 5(P5), 10(P10) ou 15(P15) segundos, com 1 min de espera, seguido por 700mW/cm² por 20s. Para o teste de união push-out (n=10), os valores de resistência de união foram obtidos em máquina de ensaio universal Instron. Para o ensaio de dureza Knoop (n=5) os espécimes foram fotoativados pelos mesmos protocolos utilizados no ensaio de resistência de união. As medidas de dureza foram realizadas em um microdurômetro (Shimadzu) em 6 profundidades (topo, 1, 2, 3, 4 e 5 mm). Os dados foram submetidos à Análise de Variância e ao teste de Tukey com nível de significância de 5 por cento. Os resultados mostraram que P5 e CL apresentaram resistência de união estatisticamente superior a todos os grupos. Não houve diferença entre os grupos P2, P3, P10, P15 e CH. Para dureza Knoop, CH apresentou os maiores valores, estatisticamente superiores a P2 e CL até 4 mm. A partir de 3 mm, a dureza de todos os grupos foi inferior a dureza do topo. O tempo de exposição inicial para o modo pulse-delay pode influenciar a resistência de união e a dureza Knoop.

Prótese total pela técnica da zona neutra / Total prótese for the technique of the neutral zone

O uso da técnica da zona neutra tem demonstrado bastante eficiência clínica, principalmente em prótese total mandibular, onde a reabsorção do rebordo apresenta-se bastante grande. Esta técnica permite distribuir os dentes artificiais, de forma adequada biomecanicamente em relação ao rebordo alveolar e à musculatura paraprotética, proporcionando assim, melhores resultados estéticos, fonéticos e maior facilidade de adaptação. Como esta técnica proporciona maior conforto ao paciente, o grau de satisfação em relação ao tratamento é maior.

Cisto odontogênico calcificante / Calcifying odontogenic cyst

Trata-se de um caso clínico típico do cisto odontogênico calcificante, ocorrido em pacientes do sexo masculino, 53 anos, leucoderma, com lesão localizada na região de primeiro bicúspide inferior esquerdo, que após biópsia foi removido por enucleação. O objetivo deste trabalho é acrescentar à literatura mais um caso clínico de COC e, assim, colaborar com outros estudos, frente a esta entidade